炸药参数对高锰钢爆炸硬化性能的影响

胡晓艳 沈兆武 刘迎彬 刘天生

胡晓艳, 沈兆武, 刘迎彬, 刘天生. 炸药参数对高锰钢爆炸硬化性能的影响[J]. 爆炸与冲击, 2015, 35(2): 255-260. doi: 10.11883/1001-1455(2015)02-0255-06
引用本文: 胡晓艳, 沈兆武, 刘迎彬, 刘天生. 炸药参数对高锰钢爆炸硬化性能的影响[J]. 爆炸与冲击, 2015, 35(2): 255-260. doi: 10.11883/1001-1455(2015)02-0255-06
Hu Xiao-yan, Shen Zhao-wu, Liu Ying-bin, Liu Tian-sheng. Influence of explosive parameter on the performance of explosion hardening of Hadifield steel[J]. Explosion And Shock Waves, 2015, 35(2): 255-260. doi: 10.11883/1001-1455(2015)02-0255-06
Citation: Hu Xiao-yan, Shen Zhao-wu, Liu Ying-bin, Liu Tian-sheng. Influence of explosive parameter on the performance of explosion hardening of Hadifield steel[J]. Explosion And Shock Waves, 2015, 35(2): 255-260. doi: 10.11883/1001-1455(2015)02-0255-06

炸药参数对高锰钢爆炸硬化性能的影响

doi: 10.11883/1001-1455(2015)02-0255-06
基金项目: 国家自然科学基金项目(11072222)
详细信息
    作者简介:

    胡晓艳(1985—), 女, 博士研究生, huxy85@mail.ustc.edu.cn

  • 中图分类号: O346.4

Influence of explosive parameter on the performance of explosion hardening of Hadifield steel

  • 摘要: 为了研究炸药参数对高锰钢爆炸硬化效果的影响,对两种不同密度的炸药进行爆速测试,并利用该炸药分别对高锰钢试样进行爆炸硬化实验,测试了从硬化表面向材料内部的硬度、抗拉强度和冲击韧性随深度的变化。测试结果表明:高锰钢试样在相同深度下,经过密度1.38 g/cm3炸药3次爆炸硬化得到的硬度大于密度1.48 g/cm3炸药2次爆炸硬化后的硬度,而冲击韧性小于密度1.48 g/cm3炸药作用后的冲击韧性;从爆炸硬化表面向下15 mm内,经过密度1.38 g/cm3炸药3次爆炸硬化得到的抗拉强度大于密度1.48 g/cm3炸药2次爆炸硬化后的抗拉强度,但深度大于15 mm时,经过密度1.38 g/cm3炸药3次爆炸硬化得到的抗拉强度小于密度1.48 g/cm3炸药2次爆炸硬化后的抗拉强度。从硬化后试件的硬度、抗拉强度以及冲击韧性这3方面考虑,使用单次爆炸冲量较小的炸药进行多次爆炸硬化效果较好。
  • 图  1  炸药测速装置

    Figure  1.  Assembly detonation velocity experiment

    图  2  实验装置图

    Figure  2.  Assembly experimental system

    图  3  爆炸硬化后试件的硬度

    Figure  3.  Hardness variation of sample explosion hardened

    图  4  爆炸硬化后试件的抗拉强度

    Figure  4.  Tensile strength of sample explosion hardened

    图  5  爆炸硬化后试件的冲击韧性

    Figure  5.  Impact toughness of sample explosion hardened

    表  1  炸药爆速测试结果

    Table  1.   Experimental result of detonation velocity

    ρ/(g·cm-3)D1/(km·s-1)D2/(km·s-1)D3/(km·s-1)D/(km·s-1)
    1.386.4806.4356.4956.470
    1.487.2107.1757.2157.200
    下载: 导出CSV
  • [1] 张观军, 杨涤心, 魏世忠, 等.高锰钢爆炸硬化[J].热加工工艺, 2006(12): 62-65. http://d.wanfangdata.com.cn/Periodical/rjggy200624021

    Zhang Guan-jun, Yang Di-xin, Wei Shi-zhong, et al. Explosion hardening of high manganese steel[J]. Hot Working Technology, 2006(12): 62-65. http://d.wanfangdata.com.cn/Periodical/rjggy200624021
    [2] 陈勇富, 洪有秋.高锰钢爆炸硬化[J].矿冶工程, 1986(4): 8-12.

    Chen Yong-fu, Hong You-qiu. Explosion hardening of high manganese steel[J]. Mining and Metallurgical Engineering, 1986(4): 8-12.
    [3] Macleod N A. Method of hardening manganese steel: US, 2703297[P]. 1955-03-01.
    [4] 赵士达, 陈维波.高锰钢整铸辙叉爆炸予硬化的研究[J].爆炸与冲击, 1982, 2(1): 11-23. http://www.bzycj.cn/article/id/11297

    Zhao Shi-da, Chen Wei-bo. On explosive hardening of hadfield steel rail frogs[J]. Explosion and Shock Waves, 1982, 2(1): 11-23. http://www.bzycj.cn/article/id/11297
    [5] 陈维波.塑料板状炸药[J].爆炸与冲击, 1984, 4(3): 65-70. http://www.bzycj.cn/article/id/11209

    Chen Wei-bo. Plastic sheet explosive[J]. Explosion and Shock Waves, 1984, 4(3): 65-70. http://www.bzycj.cn/article/id/11209
    [6] 陈勇富. SEP-3橡塑板片炸药[J].矿冶工程, 1994(2): 8-12; 70. http://www.cnki.com.cn/Article/CJFDTotal-KYGC402.001.htm

    Chen Yong-fu. SEP-3 rubbery-plastic sheet explosive[J]. Mining and Metallurgical Engineering, 1994(2): 8-12; 70. http://www.cnki.com.cn/Article/CJFDTotal-KYGC402.001.htm
    [7] 安二峰, 陈鹏万, 杨军.一种爆炸硬化用高聚物粘结塑性炸药及应用研究[J].含能材料, 2008(6): 734-737. http://www.cqvip.com/Main/Detail.aspx?id=29148930

    An Er-feng, Chen Peng-wan, Yang Jun. Application study on a polymer bonded plastic explosive after explosion hardening[J]. Chinese Journal of Energetic Materials, 2008(6): 734-737. http://www.cqvip.com/Main/Detail.aspx?id=29148930
    [8] Dastur Y N, Leslie W C. Mechanism of work hardening in Hadfield Manganese steel[J]. Metallurgical Transactions, 1981, 12(5): 749-759. doi: 10.1007/BF02648339
    [9] Hutchinson B, Ridley N. On dislocation accumulation and work hardening in Hadfield steel[J]. Scripta Materialia, 2006, 55(4): 299-302. http://www.sciencedirect.com/science/article/pii/S1359646206003678
    [10] Murr L E, Meyers M A, Niou C, et al. Shock-induced deformation twinning in tantalum[J]. Acta Materialia, 1997, 45(1): 157-175. doi: 10.1016/s1359-6454(96)00145-0
    [11] 薛继仁, 于启湛, 史春元.高锰钢爆炸加工硬化及其硬化机理[J].大连铁道学院学报, 1997(4): 67-71. http://www.cqvip.com/QK/96354A/19974/1004654553.html

    Xue Ji-ren, Yu Qi-zhan, Shi Chun-yuan. Explosive hardening and it's mechanism on manganese steel[J]. Journal of Dalian Railway Institute, 1997(4): 67-71. http://www.cqvip.com/QK/96354A/19974/1004654553.html
    [12] 陈富生.高锰钢爆炸硬化机理实验研究[J].武汉钢铁学院学报, 1991(4): 390-392.

    Chen Fu-sheng. An experimental study on explosion hardening of high Mn steels[J]. Journal of Wuhan Steel Science Institute, 1991(4): 390-392.
    [13] 陈勇富, 梁季夫, 陶颂霖.高锰钢爆炸硬化机理研究[J].江西有色金属, 1993(2): 55-56; 54.

    Chen Yong-fu, Liang Ji-fu, Tao Song-lin. Research of explosion hardening mechanism of high Mn steels[J]. Jiangxi Nonferrous Metals, 1993(2): 55-56; 54.
    [14] Zhang Fu-cheng, Lü Bo, Wang Tian-sheng, et al. Microstructure and properties of purity high Mn steel crossing explosion hardened[J]. ISIJ International, 2008, 48(12): 1766-1770. doi: 10.2355/isijinternational.48.1766
    [15] Zhang F C, Lü B, Wang T S, et al. Explosion hardening of Hadfield steel crossing[J]. Materials Science and Technology, 2010, 26(2): 223-229. doi: 10.1179/174328408X363263
    [16] Zhang M, Lü B, Zhang F, et al. Explosion deformation and hardening behaviours of hadfield steel crossing[J]. ISIJ International, 2012, 52(11): 2093-2095.
    [17] 李兴霞, 赵干, 张观军.高锰钢爆炸硬化机理分析[J].热加工工艺, 2013(6): 94-96.

    Li Xing-xia, Zhao Gan, Zhang Guan-jun. Analysis on explosion hardening mechanism of high manganese steel[J]. Hot Working Technology, 2013(6): 94-96.
    [18] 赵干, 李兴霞, 张观军.爆炸硬化对高锰钢滑动磨料磨损性能的影响[J].热加工工艺, 2013(8): 101-103. http://d.wanfangdata.com.cn/Periodical/rjggy201308032

    Zhao Gan, Li Xing-xia, Zhang Guan-jun. Effects of explosion hardening on sliding wear behavior of high manganese steel[J]. Hot Working Technology, 2013(8): 101-103. http://d.wanfangdata.com.cn/Periodical/rjggy201308032
    [19] 金韶华, 松全才.炸药理论[M].西安: 西北工业大学出版社, 2010.
    [20] 孟宪昌.爆炸动力学[M].太原: 太原机械学院出版社, 1984.
  • 加载中
图(5) / 表(1)
计量
  • 文章访问数:  3348
  • HTML全文浏览量:  323
  • PDF下载量:  366
  • 被引次数: 0
出版历程
  • 收稿日期:  2013-07-11
  • 修回日期:  2013-12-04
  • 刊出日期:  2015-03-25

目录

    /

    返回文章
    返回